Title Aging and Copper Corrosion By-Product Release: Role of Common Anions, Impact of Silica and Chlorine, and Mitigating Release in New Pipe
Degree Master of Engineering
Department Civil Engineering
Advisory Committee
Advisor Name Title
Edwards, Marc A. Committee Chair
Dietrich, Andrea M. Committee Member
Gallagher, Daniel L. Committee Member
Keywords
  • silica
  • cupric hydroxide
  • pre-treatment
  • aging
  • solubility
  • sorption
Date of Defense 2000-12-15
Availability unrestricted
Abstract
It is desirable to reduce leaching of copper from home plumbing because of environmental concerns and to comply with stringent regulation of copper in wastewater and drinking water. The solubility of the scale (oxidized copper rust layer) on the copper pipe wall, which directly contacts drinking water, is a key factor controlling the maximum soluble copper release. Gradual replacement of soluble Cu(OH)2 scale to less soluble scale is desirable and occurs through a process known as "aging."

The presence of sulfate, bicarbonate and orthophosphate in water can quickly convert Cu(OH)2 to less soluble solids. In some cases, this produces a desirable short-term reduction in copper solubility, but over longer time periods formation of these solids can be detrimental because they interfere with formation of very low solubility tenorite (CuO)or malachite phases. Likewise, silica present in water can sorb to Cu(OH)2 and hinder aging to low solubility tenorite, while the presence of chlorine can hasten aging by a chemical reaction with cupric species that has never been previously observed in the drinking water field. Mild chemical treatments that might be used to accelerate aging, and which could be applied to reduce environmental impacts of newly installed copper pipe, were successfully tested. Chemical pretreatments using lime, caustic, soda ash or chlorine reduced copper release by as much as 84% compared to new pipes without pretreatment.

Files
  Filename       Size       Approximate Download Time (Hours:Minutes:Seconds) 
 
 28.8 Modem   56K Modem   ISDN (64 Kb)   ISDN (128 Kb)   Higher-speed Access 
  etd.pdf 98.08 Kb 00:00:27 00:00:14 00:00:12 00:00:06 < 00:00:01
  etd2.pdf 1.03 Mb 00:04:44 00:02:26 00:02:08 00:01:04 00:00:05

Browse All Available ETDs by ( Author | Department )

dla home
etds imagebase journals news ereserve special collections
virgnia tech home contact dla university libraries

If you have questions or technical problems, please Contact DLA.