Title Influence of grain size, morphology and aggregation on galena dissolution
Degree PhD
Department Geosciences
Advisory Committee
Advisor Name Title
Hochella, Michael F. Jr. Committee Chair
Aruguete, Deborah Committee Member
Rimstidt, james Donald Committee Member
Schreiber, Madeline E. Committee Member
Keywords
  • galena (PbS)
  • nanoparticle
  • size
  • morphology
  • aggregation
  • high-resolution transmission electron microscopy (
  • dissolution
Date of Defense 2009-01-30
Availability unrestricted
Abstract
The acidic, non-oxidative dissolution of galena nanocrystals has been studied using both microscopic and wet-chemical methods. The effects of particle size, shape, aggregation state, and grain proximity on dissolution rates were investigated. Nearly monodisperse galena nanocrystals with an average diameter of 14.4 nm and a truncated cubic shape were synthesized. In the dissolution experiments of dispersed nanocrystals, galena nanocrystals attached on the surface of a TEM grid were exposed to deoxygenated HCl solutions (pH 3) at 25 °C. Capping groups on nanocrystals were removed via a washing process, and chemistry of nanocrystals was examined using X-ray photoelectron spectroscopy (XPS). The evolution of the size and shape of the pre- and post-dissolution nanocrystals were studied using transmission electron microscopy (TEM), and the dissolution rate was calculated directly according to the size shrinking of galena nanocrystals. To assess the size effect, galena microcrystals (~ 3 μm) were synthesized and dissolved under similar conditions to the dispersed nanocrystals. The results showed that the nanocrystals dissolved at a surface area normalized rate of one order of magnitude faster than the microcrystals. In addition, dissolution rate is orientationdependent on a single nanocrystal. High-resolution TEM (HRTEM) images indicated the {111} and {110} faces dissolve faster than {100} faces on galena nanocrystals,

rationalized by the average coordination number of ions on each of these faces. To assess the aggregation effect, dissolution experiments of aggregated galena nanocrystals were conducted using a wet-chemical method, and the results were compared with the rates of microcrystals and dispersed nanocrystals. These experiments showed that the rate of aggregated nanocrystals is in the same order of magnitude as the rate of microcrystals, but one order of magnitude smaller than that of dispersed nanocrystals. Finally, the effect of the close proximity between nanocrystals on dissolution was observed by HRTEM.

Dissolution was greatly inhibited on nanocrystal surfaces that were closely adjacent (1-2nm, or less) to other nanocrystals, which is probably relevant to the slow dissolution of aggregated nanocrystals. The dissolution phenomena of galena nanocrystals observed in this study is likely important for understanding the environmental fate and behavior of nanoparticles in aquatic systems.

Files
  Filename       Size       Approximate Download Time (Hours:Minutes:Seconds) 
 
 28.8 Modem   56K Modem   ISDN (64 Kb)   ISDN (128 Kb)   Higher-speed Access 
  Liu_dissertation.pdf 2.87 Mb 00:13:18 00:06:50 00:05:59 00:02:59 00:00:15

Browse All Available ETDs by ( Author | Department )

dla home
etds imagebase journals news ereserve special collections
virgnia tech home contact dla university libraries

If you have questions or technical problems, please Contact DLA.