Title Tribopolymerization: Anti-Wear Behavior of New High Temperature Additive Classes
Degree Master of Science
Department Mechanical Engineering
Advisory Committee
Advisor Name Title
Furey, Michael J. Committee Chair
Eiss, Norman S. Jr. Committee Member
Vick, Brian L. Committee Member
Keywords
  • anti-wear
  • alumina
  • tribology
  • tribopolymerization
  • lubrication
  • ceramics
Date of Defense 1997-08-19
Availability restricted
Abstract
Advanced ceramic materials have found many new applications in the automotive and other industries. To satisfy demands of higher temperatures and inert surfaces, new lubrication methods for these ceramics need explored and evaluated. This thesis focuses on a boundary lubrication method termed tribopolymerization -- the formation of polymers at the tribological interphase. The research evaluated new high-temperature classes of anti-wear additives. The work involved experiments on steel and alumina material pairs with a pin-on-disk tribometer used to explore the anti-wear capabilities of selected additives in the liquid phase at concentrations of 1% by weight in hexadecane.

New additives included aromatic compounds with various pendant groups adding the design functionality necessary for in-situ polymerization. The amino, hydroxyl, acid, and ester functional groups underwent studies across several aromatic molecular compositions while new heterocyclic additives, in particular the readily available lactams, underwent exploratory tests as a new class under the tribopolymerization design approach. In concentrations of 1%, additives showed significant wear reductions of up to 99.9 %. Anti-wear behavior persisted in select cases at concentrations as low as 0.1% by weight. Compounds from two new classes demonstrated anti-wear behavior at 6x the frictional heat generation of standard exploratory conditions. This surprising effect partially filled a void in the effective range of operating conditions between 0.25 m/s, 40 N and 1.0 m/s, 160 N. Earlier work by Tritt found a complete absence of anti-wear behavior for the previous additive classes at the high-speed conditions.

In addition, several individual compounds constituent to an A-R-A + B-R'-B condensation polymerization reaction demonstrated significant anti-wear behavior when used alone. In particular, the compound BTDA from DuPont's Kapton ® exhibited higher wear reductions than any other new additive.

These findings support tribopolymerization as an effective approach to boundary lubricant design. Low wear was often associated with an attached reaction debris layer. This finding is consistent with previous work involving tribopolymerization anti-wear additives with ceramics. Further research into the roles of the debris layer and tribochemistry will help in understanding the complex anti-wear behavior of these new high-temperature additive classes.

Files
  Filename       Size       Approximate Download Time (Hours:Minutes:Seconds) 
 
 28.8 Modem   56K Modem   ISDN (64 Kb)   ISDN (128 Kb)   Higher-speed Access 
[VT] 1_JJV_Thesis_1_of_3.pdf 815.36 Kb 00:03:46 00:01:56 00:01:41 00:00:50 00:00:04
[VT] 2_JJV_Thesis_2_of_3.pdf 1.41 Mb 00:06:32 00:03:22 00:02:56 00:01:28 00:00:07
[VT] 3_JJV_Thesis_3_of_3.pdf 743.15 Kb 00:03:26 00:01:46 00:01:32 00:00:46 00:00:03
[VT] indicates that a file or directory is accessible from the Virginia Tech campus network only.

Browse All Available ETDs by ( Author | Department )

dla home
etds imagebase journals news ereserve special collections
virgnia tech home contact dla university libraries

If you have questions or technical problems, please Contact DLA.