Title Combined Compression and Shear Structural Evaluation of Stiffened Panels Fabricated Using Electron Beam Freeform Fabrication
Degree Master of Science
Department Aerospace and Ocean Engineering
Advisory Committee
Advisor Name Title
Kapania, Rakesh K. Committee Chair
Hyer, Michael W. Committee Member
Philen, Michael K. Committee Member
Taminger, Karen M. Committee Member
Keywords
  • stiffener
  • buckling
  • stiffened panels
  • shear
  • compression
  • finite element analysis
  • Electron Beam Freeform Fabrication
Date of Defense 2008-06-17
Availability restricted
Abstract
Unitized aircraft structures have the potential to be more efficient than current aircraft structures. The Electron Beam Freeform Fabrication (EBF3) process can be used to manufacture unitized aircraft structures. The structural efficiency of blade stiffened panels made with EBF3 was compared to panels made by integrally machining from thick plate. The panels were tested under two load cases in a combined compression-shear load test fixture. One load case tested the panels' responses to a higher compressive load than the shear load. The second load case tested the panels' responses to an equal compressive and shear load. Finite element analysis was performed to compare with the experimental results. The EBF3 panels failed at a 18.5% lower buckling load than the machined panels when loaded mostly in compression but at an almost two times higher buckling load than the machined panels when the shear matched the compressive load. The finite element analysis was in good agreement with the experimental results prior to buckling. The results demonstrate that the EBF3 process has the capabilities of manufacturing stiffened panels that behave similarly to machined panels prior to buckling. Once the EBF3 panels buckled, the buckled shape of the EBF3 panels was different from the machined panels, generally buckling in the opposite direction of what was observed with the machined panels. This was also expected based on the finite element analysis. The different post-buckling response between the two manufacturing techniques was attributed to the residual stress and associated distortion induced during the EBF3 manufacturing process.
Files
  Filename       Size       Approximate Download Time (Hours:Minutes:Seconds) 
 
 28.8 Modem   56K Modem   ISDN (64 Kb)   ISDN (128 Kb)   Higher-speed Access 
[VT] VT_Final_Thesis.pdf 18.38 Mb 01:25:06 00:43:46 00:38:17 00:19:08 00:01:38
[VT] indicates that a file or directory is accessible from the Virginia Tech campus network only.

Browse All Available ETDs by ( Author | Department )

dla home
etds imagebase journals news ereserve special collections
virgnia tech home contact dla university libraries

If you have questions or technical problems, please Contact DLA.