Title Impact response of interleaved composite materials
Degree Master of Science
Department Engineering Mechanics
Advisory Committee
Advisor Name Title
Griffin, Odis Hayden Jr. Committee Chair
Henneke, Edmund G. II Committee Member
Loos, Alfred C. Committee Member
Keywords
  • Reinforced plastics
Date of Defense 1988-12-15
Availability restricted
Abstract

The need for better impact resistant composites has resulted in the development of many toughened resin systems. A combination of a tougher resin system along with higher strength fibers increases the impact resistance of the composite. The use of an adhesive layer between two plies of the improved prepreg system has been found to considerably increase the impact resistance. This concept is known as "Interleafing."

This investigation studies the response of the interleaf materials to instrumented drop weight impact as compared with the response of non-interleaved materials. Two non-destructive quality evaluation techniques, namely, ultrasonics and eddy currents, are used to qualitatively evaluate the damage developed in the specimens. Several different energy levels of damage are studied.

The interleaved laminate had significantly better impact response than the non-interleaved laminate for the same impact energy. The onset of delamination was delayed by the use of the interleaf. Whereas damage could be detected at an impact energy as low as 1.75 ft-lb in the baseline laminate; the interleaved laminate did not show any ultrasonic C-scan indication up to an impact of 2.45 ft-lb. The increase of delamination with increasing impact energy was slower in the interleaved specimen.

The eddy current method is not effective in detecting damage in the interleaved laminate because of the shielding effect of the interleaf. Compression Strength After Impact (CSAI) could not be used for the test laminates in this project, but the Tensile Strength After Impact test provided useful results. The tensile strength after impact of the interleaved specimen was between 20%-80% more than the baseline laminate up to impact energy of 10 ft-lb. The advantage of the interleaved specimen reduced at higher energy levels of impact.

Files
  Filename       Size       Approximate Download Time (Hours:Minutes:Seconds) 
 
 28.8 Modem   56K Modem   ISDN (64 Kb)   ISDN (128 Kb)   Higher-speed Access 
[VT] LD5655.V855_1988.G353.pdf 3.06 Mb 00:14:11 00:07:17 00:06:23 00:03:11 00:00:16
[BTD] next to an author's name indicates that all files or directories associated with their ETD are accessible from the Virginia Tech campus network only.

Browse All Available ETDs by ( Author | Department )

dla home
etds imagebase journals news ereserve special collections
virgnia tech home contact dla university libraries

If you have questions or technical problems, please Contact DLA.