Author Das, Sudipto
URN etd-08212005-151149
Title Wood/Polymeric Isocyanate Resin Interactions: Species dependence
Degree PhD
Department Macromolecular Science and Engineering
Advisory Committee
Advisor Name Title
Frazier, Charles E. Committee Chair
Glasser, Wolfgang G. Committee Member
Roman, Maren Committee Member
Wilkes, Garth L. Committee Member
Zink-Sharp, Audrey G. Committee Member
Keywords
  • wood species
  • solid-state nuclear magnetic resosnance
  • differential scanning calorimetry
  • dynamic mechanical analysis
  • thermogravimetric analysis
  • creep
  • polymeric isocyanate resin
Date of Defense 2005-07-18
Availability unrestricted
Abstract
The performance of polymeric diphenylmethane diisocyanate (PMDI) resin is known to be highly dependent on the wood species. This species dependence may be due to differences in: cure chemistry, interphase morphology, or both of these factors. This study addresses aspects of the cure chemistry and interphase morphology of wood/PMDI bondlines; specifically these effects are compared using two woods: yellow-poplar and southern pine.

In this study, the cure chemistry of wood-PMDI system was analyzed with solid state NMR (SSNMR) using wood samples cured with doubly labeled (15N,13C) PMDI resin. The kinetics of PMDI cure in the presence of wood was analyzed with differential scanning calorimetry. Thermogravimetric analysis was used to analyze the effect of resin impregnation on the degradation patterns of wood. The wood-PMDI bond morphology was probed with dynamic and static (creep) mechanical analyses in both dry and plasticized conditions. The effect of resin on wood polymer relaxations was quantitatively analyzed by both the time-temperature superposition principle and the Kohlrausch-Williams-Watts equation.

The presence of a small but statistically significant species effect was observed on both the cure chemistry and bond morphology of wood-PMDI system at low cure temperatures. The cure of PMDI resin was found to be significantly faster in pine relative to corresponding poplar samples. Resin impregnation showed a significant species dependent effect on the wood mechanical properties; the resinated pine samples showed increase in compliance while the corresponding poplar samples became stiffer.

The in situ lignin relaxation was studied with both dynamic and static modes, using plasticized wood samples. Results showed that the lignin relaxation was slightly affected by resin impregnation in both woods, but the effect was relatively larger in pine. Static experiments of dry wood samples showed a significant reduction in the interchain interactions of wood polymers in pine samples, exclusively. Investigation of plasticized pine samples, which focuses on the in situ lignin relaxations, showed only minor changes with resin impregnation. This led us to hypothesize that the large changes observed in dry samples, were due to the in situ amorphous polysaccharides. The wood-PMDI interactions were significantly reduced upon acetylation of wood. This study also discusses three new and highly sensitive methods for the analysis of wood-resin interactions.

Files
  Filename       Size       Approximate Download Time (Hours:Minutes:Seconds) 
 
 28.8 Modem   56K Modem   ISDN (64 Kb)   ISDN (128 Kb)   Higher-speed Access 
  das.pdf 6.23 Mb 00:28:49 00:14:49 00:12:58 00:06:29 00:00:33

Browse All Available ETDs by ( Author | Department )

dla home
etds imagebase journals news ereserve special collections
virgnia tech home contact dla university libraries

If you have questions or technical problems, please Contact DLA.