Title page for ETD etd-083199-185156


Type of Document Dissertation
Author Kaushiva, Bryan D.
Author's Email Address blue.bird@bigfoot.com, bryan.kaushiva@lyondell.com
URN etd-083199-185156
Title Structure-Property Relationships of Flexible Polyurethane Foams
Degree PhD
Department Chemical Engineering
Advisory Committee
Advisor Name Title
Wilkes, Garth L. Committee Chair
Conger, William L. Committee Member
Davis, Richey M. Committee Member
Marand, Eva Committee Member
Ward, Thomas C. Committee Member
Keywords
  • PTFE
  • surfactant
  • polyurethane foam
  • atomic force micros
Date of Defense 1999-08-16
Availability unrestricted
Abstract
This study examined several structure-property features of flexible polyurethane foams that are important aspects of foam production. AFM and WAXS were used to demonstrate the existence, for the first time in typical polyurethane foam systems, of lamellae-like polyurea structures ca. 0.2 mm long and ca 5-10 nm across. Aggregations of these lamellae-like hard domains may be the polyurea balls typically observed via TEM. Diethanolamine, a widely used cross-linking agent in molded foams, was shown to disrupt ordering in the polyurea hard domains and alter the interconnectivity of hard domains by preventing the formation of lamellae-like structures. These changes were shown to lead to softening of the foam. Copolymer polyol is frequently applied as reinforcing filler in foams. It was found that a common method of adding this component alters the hard segment/soft segment (HS/SS) ratio, thus increasing the load bearing capacity of the foam. It was observed in this report that at constant HS/SS ratio, the copolymer polyol only increased load bearing under humid conditions. It was also shown that the collapse of the cellular structure of a foam prior to the point of urea precipitation alters the aggregation behavior of the hard domains and alters solid-state properties. Surfactant is thus suggested to play a secondary role in the development of the hard domains by maintaining the cellular structure in the foam as the phase separation occurs and at least until the polyurethane foam has more fully organized hard segment domains. It was found that cure temperature could be manipulated to predictably change interdomain spacings and hydrogen bond development in the polymer. Curing above 100°C was found to lower hard segment content for plaques of the same formulation possibly as a result of water and isocyanate vaporization. Apart from polyurethane materials, structure-property relationships were examined in cast blends based on poly(tetrafluoroethylene) (PTFE) and the terpolymer poly(tetrafluoroethylene-co-vinylidene fluoride-co-hexafluoropropylene) (FKM). This revealed that tensile and dynamic moduli could be predictably altered by controlling the degree of FKM cross-linking or by varying PTFE content in the film. Inducing PTFE fibrillation was found to yield higher modulus films without increasing PTFE content.

Files
  Filename       Size       Approximate Download Time (Hours:Minutes:Seconds) 
 
 28.8 Modem   56K Modem   ISDN (64 Kb)   ISDN (128 Kb)   Higher-speed Access 
  KAUSHIVA1.PDF 3.84 Mb 00:17:46 00:09:08 00:07:59 00:03:59 00:00:20

Browse All Available ETDs by ( Author | Department )

dla home
etds imagebase journals news ereserve special collections
virgnia tech home contact dla university libraries

If you have questions or technical problems, please Contact DLA.