Title Sintering of Micro-scale and Nanscale Silver Paste for Power Semiconductor Devices Attachment
Degree PhD
Department Electrical and Computer Engineering
Advisory Committee
Advisor Name Title
Lu, Guo-Quan Committee Chair
Davis, Richey M. Committee Member
Guido, Louis J. Committee Member
Liu, Yilu Committee Member
Van Wyk, Daan Committee Member
Keywords
  • low-temperature sintering
  • Power packaging
  • nanoscale silver paste
  • die-attach
  • high-temperature application
Date of Defense 2005-09-02
Availability unrestricted
Abstract
Die attachment is one of the most important processes in the packaging of power semiconductor devices. The current die-attach materials/techniques, including conductive adhesives and reflowed solders, can not meet the advance of power conversation application. Silver paste sintering has been widely used in microelectronics and been demonstrated the superior properties. The high processing temperature, however, prevents its application of interconnecting power semiconductor devices. This research focuses processing and characterization of micron-scale and nanoscale silver paste for power semiconductor devices attachment.

Lowering the processing temperature is the essential to implement sintering silver paste for power semiconductor devices attachment. Two low-temperature sintering techniques - pressure-assisted sintering micro-scale silver paste and sintering nanoscale silver paste without external pressure - were developed. With the large external pressure, the sintering temperature of micro-scale silver paste can be significantly lowered. The experimental results show that by using external pressure (>40MPa), the commercial micro-scale silver paste can be sintered to have eighty percent relative density at 240oC, which is compatible with the temperature of solder reflowing. The measured properties including electrical conductivity, thermal conductivity, interfacial thermal resistance, and the shear strength of sintered silver joints, are significantly better than those of the reflowed solder layer. Given only twenty percent of small pores in the submicron range, the reliability of the silver joints is also better than that of the solder joints under the thermal cycled environment. The large external pressure, however, makes this technique difficult to automatically implement and also has a potential to damage the brittle power semiconductor devices.

Reducing silver particles in the paste from micro-size to nanoscale can increases the sintering driving force and thus lowers the sintering temperature. Several approaches were developed to address sintering challenges of nanoscale silver particles, such as particles aggregation and/or agglomeration, and non-densification diffusion at low temperature. These approaches are : nanoscale silver slurry, instead of dry silver powder, is used to keep silver particles stable and prevent their aggregation. Ultrasonic vibration, instead of conventional ball milling, is applied to disperse nanoscale silver particles in the paste from to avoid from agglomerating. Selected organics in the paste are applied to delay the onset of mass-diffusion and prevent non-densification diffusion at low temperature. The measured results show that with heat-treatment at 300oC within one hour, the sintered nanoscale silver has significantly improved electrical and thermal properties than reflowed solders. The shear strength of sintered silver interconnection is compatible with that of solder.

The low-temperature sinterable nanoscale silver paste was applied to attach the bare Silicon carbide (SiC) schottky barrier diode (SBD) for high temperature application. Limited burn-out path for organics in the silver layer challenges the sintering die-attach. This difficulty was lessened by reducing organics ratio in the silver paste. The effects of die-size and heating rate on sintering die-attach were also investigated. The single chip packaging of SiC SBD was fabricated by sintering die-attach and wire-bonding. The tested results demonstrate that the sintering nanoscale silver paste can be applied as a viable die-attach solution for high-temperature application.

Files
  Filename       Size       Approximate Download Time (Hours:Minutes:Seconds) 
 
 28.8 Modem   56K Modem   ISDN (64 Kb)   ISDN (128 Kb)   Higher-speed Access 
  Dissertation_Zhiye__Zhang.pdf 5.71 Mb 00:26:26 00:13:35 00:11:53 00:05:56 00:00:30

Browse All Available ETDs by ( Author | Department )

dla home
etds imagebase journals news ereserve special collections
virgnia tech home contact dla university libraries

If you have questions or technical problems, please Contact DLA.