Title Assembly of Conductive Colloidal Gold Electrodes on Flexible Polymeric Substrates using Solution-Based Methods
Degree PhD
Department Macromolecular Science and Engineering
Advisory Committee
Advisor Name Title
Claus, Richard O. Committee Chair
Inman, Daniel J. Committee Member
Leo, Donald J. Committee Member
Long, Timothy E. Committee Member
Love, Brian J. Committee Member
Keywords
  • flexible substrates
  • thin film
  • solution-based assembly
  • colloidal gold
  • conductive
Date of Defense 2005-10-19
Availability unrestricted
Abstract
This work describes the techniques of assembling colloidal gold on flexible polymeric substrates from solution. The process takes advantage of the strong affinity of gold to thiol and amino groups. Polymeric substrates were modified with silanes having these functional groups prior to Au attachment or in the case of poly(urethane urea) (PUU), no surface functionalization was required. This polymer has terminal amine and N-H groups on the polymer chain, which can act as coordination points for gold. Immersion in the colloidal gold solution led to the formation of a monolayer. Increased coverage was obtained by two methods. The first was a reduction or "seeding" process, where Au was reduced onto the attached particles on the surface. The second was using different linker molecules and creating a multilayered film by a layer-by-layer assembly. Three linker molecules of different lengths were used. Films fabricated using the smallest molecule had the least resistance whereas films fabricated with the longest molecule were not conductive. The resistance of these films may be varied easily by heating. Heating the films at temperatures as low as 120 °C caused a dramatic decrease in the resistance of over six orders in magnitude. Successful attachment of gold to PUU with very good adhesion properties was also demonstrated. The attachment of gold was stable in different solvents. Upon stretching the PUU-Au films, it was observed that there is a reversible resistance increase with strain and at a certain strain, the film becomes non-conductive. This sharp transition from conductive to insulating has potential applications in flexible switches and sensors. A hysteresis in the strain-resistance curves, analogous to the hysteresis in the stress-strain curves of the polymer was also observed. Using PUU as an adhesive agent, gold electrodes were successfully assembled on Nafion-based polymer transducers. These materials showed comparable actuation behavior to the electrodes made by the Pt-reduction method, with the added advantage of the ability to form patterned electrodes for distributed transducers. Patterning techniques were developed to form colloid-polymer multilayers for use in photonic crystal materials using selective deposition on patterned silane monolayers. Patterns of gold electrodes were also made on flexible polymers using a photoresist-based method.

Files
  Filename       Size       Approximate Download Time (Hours:Minutes:Seconds) 
 
 28.8 Modem   56K Modem   ISDN (64 Kb)   ISDN (128 Kb)   Higher-speed Access 
  Supriya_Dissertation.pdf 6.05 Mb 00:28:01 00:14:24 00:12:36 00:06:18 00:00:32

Browse All Available ETDs by ( Author | Department )

dla home
etds imagebase journals news ereserve special collections
virgnia tech home contact dla university libraries

If you have questions or technical problems, please Contact DLA.