Title Energy Absorption Capacity of Graphite-Epoxy Composite Tubes
Degree Master of Science
Department Engineering Mechanics
Advisory Committee
Advisor Name Title
Hyer, Michael W. Committee Chair
Lesko, John Jack Committee Member
Loos, Alfred C. Committee Member
Keywords
  • static
  • dynamic
  • low-cost
  • filament winding
  • towpreg
  • 12k
  • 50k
Date of Defense 1998-11-11
Availability unrestricted
Abstract
The energy absorption capacity of a series of axially crushed composite tubes fabricated from high tow count graphite fiber is compared with those of similar tubes fabricated from aerospace-grade fiber to determine the viability of considering the use of such fibers in automotive applications. To that end, graphite-epoxy tubular specimens with circular and square cross-sectional geometries; stacking sequences with ±45° fibers and with both ±45° and 0° fibers; and two different fiber types were fabricated and crushed both statically and dynamically to examine the energy absorption characteristics. The fiber types, in the form of preimpregnated tow (towpreg) from Thiokol, were Akzo Fortafil 50k fiber and aerospace-grade T300 12k fiber. Using the towpreg, sixteen tubes were filament wound on aluminum mandrels. Three specimens were cut from each of these tubes for a total of forty-eight specimens. Twenty-four of these specimens were crushed statically in a load frame and twenty-four were crushed dynamically in a drop fixture. In order to characterize the tubes and specimens, a number of measurements were taken. These measurements included length, wall thickness, cross-sectional dimensions, volume, and mass. Two important energy absorption measures were examined: the specific energy absorption (SEA) and the ratio of the peak load to the average load. The geometry had a significant effect on the energy absorption but the stacking sequence did not. It was also found that the 50k material was less effective at absorbing energy than the 12k material, but the 50k still may be acceptable.

Files
  Filename       Size       Approximate Download Time (Hours:Minutes:Seconds) 
 
 28.8 Modem   56K Modem   ISDN (64 Kb)   ISDN (128 Kb)   Higher-speed Access 
  Thesis.pdf 1.75 Mb 00:08:05 00:04:09 00:03:38 00:01:49 00:00:09

Browse All Available ETDs by ( Author | Department )

dla home
etds imagebase journals news ereserve special collections
virgnia tech home contact dla university libraries

If you have questions or technical problems, please Contact DLA.