Title:Analysis of Cyanate Ester Resins and Graphite Fabric for Use in Resin Film Infusion Processing
Degree:Master of Science
Department:Materials Science and Engineering
Committee Chair: Dr. Alfred C. Loos
Chair's email:aloos@vt.edu
Committee Members:Dr. R. G. Kander
Dr. B. J. Love
Keywords:Cyanate Esters, Cure-Kinetics, Graphite Fiber Composites, Resin Film Infusion
Date of defense:December 16, 1997
Availability:Release the entire work for Virginia Tech access only.
After one year release worldwide only with written permission of the student and the advisory committee chair.

Abstract:

The objective of this investigation was to characterize two cyanate ester resins and a eight harness satin (8HS) graphite fabric for use in resin film infusion (RFI) processing. Two cyanate ester resin systems were characterized to determine their cure-kinetics, and viscosities during cure. A 8HS graphite fabric was tested in compaction and through the thickness permeability. A one-dimensional, through the thickness, flow and cure computer simulation was run.

The resin cure-kinetics models predicted the curing behavior of the resins as functions of time, temperature, and degree of cure. The proposed viscosity models determined the resin viscosity as a function of temperature and degree of cure. The 8HS graphite fabric was tested in compaction and through the thickness permeability to determine the effect of compaction pressure on fiber volume fraction and in turn on through the thickness permeability. The one-dimensional RFI flow and cure simulation combined the cure-kinetics and viscosity models of the resins with the characteristics of the graphite fabric and determined resin infiltration and cure times.

The proposed cure-kinetics and viscosity models were more than adequate in modeling the cure and flow behavior of the cyanate ester resin systems. Power law curve fits accurately represented the compaction and through the thickness permeability of the 8HS graphite fabric. Finally, the one-dimensional RFI flow and cure simulation showed that resin viscosity was the major influence on the infiltration times.


List of Attached Files

etd.pdf

At the author's request, all materials (PDF files, images, etc.) associated with this ETD are accessible from the Virginia Tech network only.


The author grants to Virginia Tech or its agents the right to archive and display their thesis or dissertation in whole or in part in the University Libraries in all forms of media, now or hereafter known. The author retains all proprietary rights, such as patent rights. The author also retains the right to use in future works (such as articles or books) all or part of this thesis or dissertation.