Title:Aspects of Wood Adhesion: Applications of 13C CP/MAS NMR and Fracture Testing
Degree:Doctor of Philosophy
Department:Wood Science and Forest Products
Committee Chair: Dr. C.E. Frazier
Chair's email:cfrazier@vt.edu
Committee Members:Wolfgang G. Glasser
Frederick A. Kamke
Thomas C. Ward
James P. Wightman
Keywords:PF, phenol formaldehyde, isocyanate, pMDI, IPN, interpenetrating network formation, mechanisms of adhesion
Date of defense:January 28, 1998
Availability:Release the entire work immediately worldwide.

Abstract:

Phenol Formaldehyde (PF) and polymeric isocyanate (pMDI) are the two main types of adhesives used in the production of structural wood-based composites. Much is unknown about various aspects of adhesion between these two types of resins and wood. The present research describes the development of techniques which will permit an enhanced understanding of 1.) the extent of cure of PF within a wood based composite, 2.) the scale of molecular level interactions between PF and pMDI and wood, 3.) mechanical performance and durability of wood-adhesive bonds. Correlations were established between conventional methods of characterization of neat PF (thermomechanical analysis, swelling studies) and measurements made using 13C CP/MAS NMR. These correlations were then utilized to characterize PF cured in the presence of wood. The use of 13C labeled PF allowed estimates of relative degrees of resin conversion to be made. The use of 13C and deuterium labeled PF allowed qualitative estimates of resin molecular rigidity to be made. The scale of molecular level interactions between PF and pMDI and wood was probed using NMR relaxation experiments. Evidence was shown to suggest the formation of an interpenetrating polymer network (IPN) morphology existing at both types of wood-resin interphases. The formation of the IPN morphology was strongly influenced by resin molecular weight, cure temperature and the presence of solvent. A new test geometry for the evaluation of the fracture toughness of wood-adhesive bonds was developed. Consistent and reliable results were obtained. It was found that low molecular weight PF possessed enhanced durability over high molecular weight.

List of Attached Files

SCHMIDT.PDF


The author grants to Virginia Tech or its agents the right to archive and display their thesis or dissertation in whole or in part in the University Libraries in all forms of media, now or hereafter known. The author retains all proprietary rights, such as patent rights. The author also retains the right to use in future works (such as articles or books) all or part of this thesis or dissertation.