STRESS AND FATIGUE ANALYSIS OF SVI-TESTED CAMSHAFT LOBES

by

Jose Alejandro Escobar

Thesis submitted to the Faculty of the Virginia Tech in partial fulfillment of the requirements for the degree of

Master of Science in Materials Science and Engineering

in

Materials Science and Engineering

Approved

Robert W. Hendricks, Chair
Ronald W. Landgraf
Stephen L. Kampe
William T. Reynolds

November 8, 1996
Blacksburg, Virginia


Abstract

Nondestructive evaluation techniques were employed to fully characterize three 2.3L camshafts tested in an engine simulator for an equivalent of 100,000 miles. Optical microscopy, acoustic microscopy (SAM), and profilometry were used to characterize wear and fatigue, crack depth, and surface roughness, respectively. Results show cracking to occur mainly in the opening ramp of the most abusively ground cam lobes. No clear evidence was found for subsurface cracking at depths as great as 200 mm from the lobešs surface. Profilometry results show no evidence of any major tribological effect due to the sliding friction of the follower. Fractography studies show a difference between fracture surfaces among the cracks examined; straight cracks exhibit features resembling fatigue propagation, while fracture surfaces from pitted cracks show a more brittle behavior. Small grinding cracks (approximately 300 mm in length) were found in the opening ramps of the most abusively ground lobes prior to testing. Knoop and Nanoindenter microhardness indicate a near-surface rehardening for the most abusively ground lobe (confirmed by metallography), and temper burn for the remaining lobes. X-ray residual stress results made in the opening ramp of the tested lobes show evidence of residual stress relaxation. X-ray line width data as a function of depth does not correlate with residual stress.

Full text (PDF) 3,794,641 Bytes


The author grants to Virginia Tech or its agents the right to archive and display their thesis or dissertation in whole or in part in the University Libraries in all forms of media, now or hereafter known. The author retains all proprietary rights, such as patent rights. The author also retains the right to use in future works (such as articles or books) all or part of this thesis or dissertation.
[ETD main page] [Search ETDs][etd.vt.edu] [SCP home page] [library home page]

Send Suggestions or Comments to webmaster@scholar.lib.vt.edu