Scaling Effects on Damage Development, Strength, and Stress-Rupture Life of Laminated Composites in Tension

by

J. Andre Lavoie

PhD Dissertation submitted to the Faculty of the Virginia Tech in partial fulfillment of the requirements for the degree of

Doctor of Philosophy

in

Engineering Mechanics

Approved

John Morton

April 4, 1997
Blacksburg, Virginia


Abstract

The damage development and strength of ply-level scaled carbon/epoxy composite laminates having stacking sequence of [+Tn/-Tn/902n]s where constraint ply angle, T, was 0, 15, 30, 45, 60, and 75 degrees, and size was scaled as n=1,2,3, and 4, is reported in Part I. X-radiography was used to monitor damage developments. First-ply failure stress, and tensile strength were recorded. First-ply failure of the midplane 90 deg. plies depended on the stiffness of constraint plies, and size. All 24 cases were predicted using Zhang’s shear-lag model and data generated from cross-ply tests. Laminate strength was controlled by the initiation of a triangular-shaped local delamination of the surface angle plies. This delamination was predicted using O’Brien’s strain energy release rate model for delamination of surface angle plies. For each ply angle, the smallest laminate was used to predict delamination (and strength) of the other sizes.

The in-situ tensile strength of the 0 deg. plies within different cross-ply, and quasi-isotropic laminates of varying size and stacking sequence is reported in Part II. No size effect was observed in the strength of 0 deg. plies for those lay-ups having failure confined to the gauge section. Laminates exhibiting a size-strength relationship, had grip region failures for the larger sizes. A statistically significant set of 3-point bend tests of unidirectional beams were used to provide parameters for a Weibull model, to re-examine relationship between ultimate strength of 0 deg. plies and specimen volume. The maximum stress in the 0 deg. plies in bending, and the tensile strength of the 0 deg. plies (from valid tests only) was the same. Weibull theory predicted loss of strength which was not observed in the experiments.

An effort to model the durability and life of quasi-isotropic E-glass/913 epoxy composite laminates under steady load and in an acidic environment is reported in Part III. Stress-rupture tests of unidirectional coupons immersed in a weak hydrochloric acid solution was conducted to determine their stress-life response. Creep tests were conducted on unidirectional coupons parallel and transverse to the fibers, and on ±45 deg. layups to characterize the lamina stress- and time-dependent compliances. These data were used in a composite stress-rupture life model, based on the critical element modeling philosophy of Reifsnider, to predict the life of two ply-level thickness-scaled quasi-isotropic laminates.


List of attached files

File NameSize (Bytes)
etd-part1.pdf
Abstract, Table of Contents and Part I: Effects of Size, Constraint and Thickness, on Damage Initiation, Growth, and Strength of [+ Øn /- Øn /902n ]s Composite Laminates
8,886,565 Bytes
etd-part2.pdf
Part II: Strength Scaling of Composite Laminates Amidst Invariant 0° Ply Strength
1,817,746 Bytes
etd-part3.pdf
Part III: Prediction of Stress-Rupture Life of Glass/Epoxy Laminates in an Acidic Environment from Lamina Behavior
2,750,689 Bytes


The author grants to Virginia Tech or its agents the right to archive and display their thesis or dissertation in whole or in part in the University Libraries in all forms of media, now or hereafter known. The author retains all proprietary rights, such as patent rights. The author also retains the right to use in future works (such as articles or books) all or part of this thesis or dissertation.
[ETD main page] [Search ETDs][etd.vt.edu] [SCP home page] [library home page]

Send Suggestions or Comments to webmaster@scholar.lib.vt.edu