Scholarly
    Communications Project


Document Type:Master's Thesis
Name:Thomas A. Kuhr
Email address:tkuhr@vt.edu
URN:1997/00192
Title:Adhesion Strength of Cordierite Bulk Coatings on Molybdenum Substrates
Degree:Masters of Science
Department:Materials Science and Engineering
Committee Chair: Dr. Gou-Quan Lu
Chair's email:gqlu@vt.edu
Committee Members:
Keywords:interfacial fracture toughness, adhesion, ceramic-metal bonds
Date of defense:July 23, 1997
Availability:Release the entire work immediately worldwide.

Abstract:

Cordierite was adhered to molybdenum using various metallic interlayers of copper, nickel, and chromium. The development of a coating adhesion test methodology was required to choose between interface designs. An indentation method was chosen because of ease in testing and availability of fracture mechanics interpretations of test data. The interfacial fracture toughness was determined from indentation load vs. crack length data by examining the residual stress and critical buckling load of the ceramic coatings. The interfacial fracture toughness values obtained using a slightly different indentation analysis agree with those in the literature. Quantitative chemical analysis of the interface microstructure was used to explain differences in interfacial fracture toughness values for samples with different metallic interlayer designs. The best interface design for adhering cordierite glass-ceramic coatings to molybdenum was found to be molybdenum / 2 mm copper / 4 mm chromium / cordierite.

List of Attached Files

thesis.pdf


The author grants to Virginia Tech or its agents the right to archive and display their thesis or dissertation in whole or in part in the University Libraries in all forms of media, now or hereafter known. The author retains all proprietary rights, such as patent rights. The author also retains the right to use in future works (such as articles or books) all or part of this thesis or dissertation.